472560 Understanding Site Isolation of Pd and Ni in Zn-Based Bulk Intermetallics during the Selective Hydrogenation of Alkynes

Thursday, November 17, 2016: 2:30 PM
Franciscan A (Hilton San Francisco Union Square)
Anish Dasgupta, Chemical Engineering, Pennsylvania State University, University Park, PA and Robert M. Rioux, Chemical Engineering, The Pennsylvania State University, University Park, PA

The catalytic semi-hydrogenation of acetylene to produce ethylene is a common method for the removal of trace acetylene (~1%) in ethylene feed streams destined for ethylene polymerization. An effective catalyst for this reaction converts all of the acetylene to ethylene without further conversion of ethylene to ethane such that there is a net increase in the amount of ethylene. Pd-Ag alloys, and more recently, intermetallic Pd-Ga compounds, demonstrate high selectivity towards ethylene and long-term stability. Improved selectivity is a result of isolation of active Pd hydrogenation sites which reduces over-hydrogenation to form ethane, oligomerization products, and coke formation on the catalyst surface. Replacing Pd-based catalysts with base metal Ni-based catalysts would be highly beneficial in terms of cost and environmental impact. Bulk intermetallic catalysts contain little structural and compositional variance, a property that is not easily attainable with supported catalysts. We report on the catalytic selectivity of unsupported bulk intermetallic Ni-Zn and Pd-Zn catalysts for acetylene semi-hydrogenation. We demonstrate the addition of Ni to Zn improves selectivity to ethylene due to a reduction in acetylene oligomerization products rather than ethane over-hydrogenation. The most selective catalysts had the lowest Ni content with a g-brass bulk structure. Structural investigation by neutron diffraction demonstrated the presence of well-defined Ni (or Pd) trimers in the g-brass structure with the number of these trimers increasing with Ni (or Pd) content. The Ni alloys are active for H2-D2 exchange, but all surfaces (i.e, different Ni content) are indistinguishable with respect to their catalytic behavior. In the case of Pd-Zn alloys with the g-brass structure, there are apparent differences in the H2-D2 rates and ethylene hydrogenation as the Pd content (and therefore number of Pd trimers) increases. While the Ni and Pd trimers are stable in the bulk structure, the differences in the surface stability of these trimers in the Zn matrix and the corresponding percentage of the trimer-containing surface present in a Wulff reconstruction explain the disparate catalytic results in the seemingly related systems. We demonstrate bulk intermetallics are useful systems to screen compositional and structural (from site-isolated to well-defined 2D clusters) variance on catalytic behavior. Transforming the bulk intermetallic structure into its nanoscale analog still remains a critical challenge for catalyst synthesis.

Extended Abstract: File Not Uploaded
See more of this Session: Atomically Dispersed Supported Metal Catalysts I
See more of this Group/Topical: Catalysis and Reaction Engineering Division