460638 Hydrogen Production Via Photocatalytic Water Splitting over Mesoporous Pt/TiO2

Thursday, November 17, 2016: 8:50 AM
Franciscan B (Hilton San Francisco Union Square)
Fabricio Guayaquil Sosa, Chemical and Biochemical Engineering Department, University of Western Ontario, London Ontario, ON, Canada, Benito Serrano, Chemical Engineering, Universidad Autonoma de Zacatecas., Zacatecas., Mexico and Hugo de Lasa, Chemical Reactor Engineering Centre, Western University, London, ON, Canada

Mesoporous TiO2 semiconductors were synthesized by sol-gel technique, using a triblock-copolymer-templating, named Pluronic F-127. In order to minimize the electron-hole pair recombination, Pt was added as an electron trap in different percentages (i.e. 1.00 wt. %, 2.50 wt. %) during the sol-gel synthesis of the TiO2 semiconductors. This was followed by calcination at 500 oC and 550 oC. Semiconductors' activity was evaluated in a bench-scale Photo-CREC-Water II (PCWII) photoreactor. In this sense, water splitting was carried out under near-UV light for hydrogen molecule production in the PCWII Reactor using ethanol at 2 % v/v as a renewable organic scavenger (electron donor). Ethanol acts as a good hole scavenger. The PCWII consisted of a 2.65 L internally irradiated slurry annular reactor with a 15 W T8 Black-Light-Blue (F15T8/BLB) lamp. The optimal photocatalyst loading was 0.15 g L-1 in acid medium (pH = 4.0). The volume of the aqueous suspension was 6.0 L. Thereby the present study shows that mesoporous TiOwith 2.50 wt. % of Pt exhibits the best activity for hydrogen production under the same photoreaction conditions. This semiconductor material showed: a) An anatase phase with XRD, b) A reduced band gap at 2.34 eV was calculated, employing UV-Vis spectroscopy and a Tauc plot, c) 10-30 nm TiOparticles with SEM-EDX, d) A 140 m2/g BET surface area as well as 10 nm and 20 nm bimodal pore size distributions. Furthermore, the absorbed photons on the photocatalysts have been studied by employing macroscopic balances. These macroscopic energy balances considered for incident, scattered and transmitted near-UV photons. In this respect, evaluated Quantum Yields (QY) displayed a promising 0.27 (27%) when utilizing mesoporous 2.50 wt. % Pt/TiO2-550oC.

Extended Abstract: File Not Uploaded
See more of this Session: Catalytic Hydrogen Generation
See more of this Group/Topical: Catalysis and Reaction Engineering Division