426389 Microwave Induced Welding of Carbon Nanotube-Thermoplastic Interfaces

Tuesday, November 10, 2015: 12:30 PM
251E (Salt Palace Convention Center)
Charles Sweeney, Texas A&M University, College Station, TX, Mohammad Saed, Electrical Engineering, Texas Tech University, Lubbock, TX and Micah Green, Chemical Engineering, Texas A&M University, College Station, TX

Three-dimensional (3D) printed parts produced by fused-filament fabrication of a thermoplastic polymer have become increasingly popular at both the commercial and consumer level. The mechanical integrity of these rapid-prototyped parts however, is severely limited by the interfillament bond strength between adjacent extruded layers. In this report we propose for the first time a method for welding thermoplastic interfaces of 3D printed parts using the extreme heating response of carbon nanotubes (CNTs) to microwave energy. To achieve this, we developed a coaxial printer filament with a pure polylactide (PLA) core and a CNT composite sheath. This produces parts with a thin electrically percolating network of CNTs at the interfaces between adjacent extruded layers. These interfaces are then welded together upon microwave irradiation at 2.45GHz. We investigated the dielectric properties of the PLA/CNT composites at microwave frequencies and performed in-situ microwave thermometry using a forward-looking infrared (FLIR) camera to characterize the heating response of the PLA/CNT composites upon microwave irradiation. Tensile tests on welds indicate substantial strengthening as a result of microwave-induced CNT heating at the interfaces. Finally, computational models were developed to verify the microwave heating response of the percolating CNT composites according to their measured dielectric properties.

Extended Abstract: File Not Uploaded
See more of this Session: Composites Technology and Processing I
See more of this Group/Topical: Materials Engineering and Sciences Division