378725 Thermochemical Dissociation of CO2 into Renewable Fuels Via CexZryHfzO2 Based Redox Reactions Using Concentrated Solar Energy

Wednesday, November 19, 2014: 4:50 PM
M101 (Marriott Marquis Atlanta)
Rahul Bhosale1, Ivo Alxneit2, Anand Kumar1, LJP van den Broeke1, Jamila Folady1, Dareen Dardor1, Shahd Gharbia1 and Mehak Jilani1, (1)Department of Chemical Engineering, Qatar University, Doha, Qatar, (2)Solar Technology Laboratory, Paul Scherrer Institute, Villigen PSI, Switzerland

Today the world's energy economy is still based to a large extent on the abundance of fossil fuels. This has led to a rapid depletion of the easily accessible oil reserves resulting in continuously rising oil prices. Furthermore severe environmental problems caused by the CO2 induced greenhouse effect have begun to become apparent. Thus, there is a pressing need to develop technologies to produce carbon free renewable fuels such as H2 or renewable precursors for fuels such as syngas (a mixture of H2 and CO). The latter can be processed to liquid fuels via the Fischer-Tropsch process. Solar radiation is an essentially inexhaustible energy source that delivers about 100000 TW to the earth. To harvest the solar radiation and to convert it effectively into renewable fuels such as H2 and syngas directly from H2O and captured CO2 provides a promising path for a future sustainable energy economy. One of the ways of producing solar fuels is by metal oxide based two-step solar thermochemical cycles. In these cycles, the first step consists of the endothermic reduction of a metal oxide at elevated temperatures releasing O2. The second step corresponds to the slightly exothermic re-oxidation of the reduced metal oxide at lower temperatures by H2O, CO2, or a mixture of the two producing H2, CO or syngas. Among many metal oxides investigated for solar fuel production, in recent years, research has been focused towards non-volatile mixed metal oxides such as doped ceria.

In this investigation, Zr and Hf doped ceria based redox materials (various doping combinations) were synthesized using a co-precipitation method. The respective metal precursors were dissolved in water. Upon complete dissolution, excess ammonium hydroxide (NH4OH) was added drop-wise to the mixture under vigorous stirring to precipitate the mixed-metal hydroxides (final pH = ~9). The obtained precipitates were filtered, washed with water until free from anion impurities and oven dried at 100oC for 8 – 10 h. Subsequently calcination was performed at different temperatures in air. The calcined powders were characterized by powder X-ray diffraction, BET surface area analysis, scanning (SEM) and transmission electron microscopy (TEM), etc. Synthesized Zr and Hf doped ceria redox materials were further tested for thermochemical CO2-splitting by using a high-temperature thermogravimetric analyzer (TGA). Multiple thermal reduction and oxidation (by CO2) cycles were performed at various operating conditions by using TGA while the O2 and CO was quantified by gas chromatography. The results related to synthesis, physiochemical characterization, and thermogravimetric experiments will be presented in detail.

Extended Abstract: File Uploaded
See more of this Session: Novel Approaches to CO2 Utilization
See more of this Group/Topical: Topical Conference: Advanced Fossil Energy Utilization