Results and Discussion: Synthesis of the pentacene derivatives was performed in a multi-step reaction scheme as shown in Scheme 1. The tetrabrominated starting materials were synthesized in moderate yields using a method similar to literature procedures [6]. These compounds underwent a Diels-Alder cyclization reaction to produce the substituted pentacene precursors. In a procedure similar to what is reported in literature [7,8], the reaction of the tetrabrominated compounds with 1,4-anthraquinone in the presence of NaI and anhydrous DMF at 60 °C afforded asymmetric quinones in 60-88% yields while reaction with p-benzoquinone under the same conditions gave symmetric quinones in slightly lower yields. The quinones were then converted to the corresponding pentacene derivatives in 38-71% yields by reduction in the presence of aluminum wire, cyclohexanol, and catalytic amounts of HgCl2 and CBr4. The crude products were purified via sublimation prior to device fabrication. In order to determine the stability of the molecules, thermal gravimetric analysis (TGA) was performed for pentacene derivatives under a stream of nitrogen gas at a heating rate of 10 °C/min. The decomposition temperature was defined as the temperature at which a 5 % weight loss takes place. We found that the decomposition temperature of 2,3-dibromopentacene (Br2P) was 15 °C higher than that of 2,3,9,10-tetrabromopentacene (Br4P), even though Br2P has a smaller molecular weight. As a result, Br2P could be purified by multi-sublimation to give enough pure compounds for the measurement of device performance; however, it was difficult to obtain pure Br4P. Top-contact thin-film transistors were fabricated on octadecyltrimethoxysilane (OTS) treated SiO2/Si substrates. Br2P and 2-cyanopentacene (CNP) were thermally evaporated at different substrate temperatures. All devices operated as p-type transistors. The field-effect mobility was calculated using the IDS values in the saturation regions. Br2P devices yielded a mobility of 0.21 cm2V-1s-1 at substrate temperatures ranging from 80-90 °C, while CNP devices exhibited mobility near 10-2 cm2V-1s-1. The field-effect mobility of Br2P increased with increasing TD, which is attributed to better ordered thin films and larger grain sizes at elevated TD. AFM images also showed sharper grain boundaries and larger crystal size for higher TD thin films. Thus, the grain sizes for Br2P was on the order of 250-400 nm at TD = 25 °C, while its sizes became bigger at 90 °C, on the order of 500-750 nm. Ongoing research of the synthesis and device performance of other pentacene derivatives is currently being conducted.
References: [1] Bao, Z. Adv. Mater. 2000, 12, 227. [2] Dimitrakopoulos, C.D.; Mascaro, D.J. IBM J. Res. & Dev. 2001, 45, 11. [3] Meng, H.; Bendikov, M.; Mitchell, G.; Helgeson, R.; Wudl, F.; Bao, Z.; Siegrist, T.; Kloc, C.; Chen, C. Adv. Mater. 2003, 15, 1090. [4] Swartz, C.R.; Parkin, S.R.; Bullock, J.E.; Anthony, J.E. Org. Lett. 2005, 7, 3163. [5] Jiang, J.; Kaafarani, B. R.; Neckers, D. C. J. Org. Chem. 2006, 71, 2155. [6] Anthony, I.; Wege, D. Aust. J. Chem. 1996, 49, 1263. [7] Morris, J.L.; Becker, C.L.; Fronczek, F.R.; Daly, W.H.; McLaughin, M.L. J. Org. Chem, 1994, 59, 6484. [8] Cava, M.P.; Shirley, R.L. J. Am. Chem. Soc. 1960, 82, 654.